Type of Dock Fender
- Type PI
- Type Cell
- Type V
Properties |
Units |
Standard |
Results |
|
| TS (Tensile Strength) | Mpa |
Min.16 |
20.4 |
|
| EB (Elongation at break) | % |
Min. 350 |
565 |
|
| M. (Modulus) | 100 |
Mpa |
- |
1.8 |
| M. (Modulus) | 200 |
Mpa |
- |
3.2 |
| M. (Modulus) | 300 |
Mpa |
- |
6.2 |
| M. (Modulus) | 400 |
Mpa |
- |
8.8 |
| M. (Modulus) | 500 |
Mpa |
- |
15.5 |
| M. (Modulus) | 600 |
Mpa |
- |
- |
| M. (Modulus) | 700 |
Mpa |
- |
- |
| M. (Modulus) | 800 |
Mpa |
- |
- |
| H. (Hardness) | Shore A |
55 ± 5 |
57 |
|
| Density | gr/ ml |
- |
- |
|
| Flex Cracking | Kcs |
- |
- |
|
| Abrasion | mm³ |
- |
- |
|
| Swelling | % |
- |
- |
|
| After Aging 100° | ||||
| TS (Tensile Strength | Mpa |
Min. 12.8 |
14.8 |
|
| EB (Elongation at break) | % |
Min. 280 |
428 |
|
| M. (Modulus) | 100 |
Mpa |
- |
2.0 |
| M. (Modulus) | 200 |
Mpa |
- |
4.4 |
| M. (Modulus) | 300 |
Mpa |
- |
7.6 |
| M. (Modulus) | 400 |
Mpa |
- |
11.2 |
| M. (Modulus) | 500 |
Mpa |
- |
- |
| M. (Modulus) | 600 |
Mpa |
- |
- |
| M. (Modulus) | 700 |
Mpa |
- |
- |
| M. (Modulus) | 800 |
Mpa |
- |
- |
| H. (Hardness) | Shore A |
55 ± 5 |
60 |
|
| Compression Set 25% | % |
- |
43.46 |
|